GHID
PRIVIND CORESPONDENTA MATERIALELOR
(valabil pentru mentenanta mijloacelor)
F115.20-04-002RA, vers 01
Uz intern : AUTOMOBILE DACIA
Data elaborarii: martie 2004
Elaborat : Vasile BAIASU
CUPRINS
1. OTELURI LAMINATE SI TRASE
1.1. OTEL DE UZ GENERAL PENTRU CONSTRUCTII
1.2. OTEL CARBON DE CALITATE PENTRU TRATAMENT TERMIC, DESTINAT CONSTRUCTIEI DE MASINI
1.3. OTEL PENTRU ARCURI
1.4. OTEL ALIAT PENTRU TRATAMENT TERMIC IN CONSTRUCTIA DE MASINI
1.5. OTEL RAPID PENTRU SCULE
1.6. OTEL PENTRU SCULE
1.7. OTEL ALIAT PENTRU SCULE
1.8. OTEL REZISTENT LA COROZIUNE SI 14414p1519o REFRACTAR, PRELUCRAT LA CALD
1.9. OTEL INOXIDABIL SI REFRACTAR
1.10. OTEL PENTRU RULMENTI
1.11. OTEL REZISTENT LA UZURA
1.12. OTEL PENTRU AUTOTURISME DACIA
1.13. OTEL PENTRU TABLE DESTINATE CAZANELOR SI RECIPIENTELOR SUB PRESIUNE, PENTRU TEMPERATURA AMBIANTA RIDICATA
1.14. OTEL PENTRU TABLE DESTINATE CAZANELOR SI RECIPIENTELOR SUB PRESIUNE, PENTRU TEMPERATURA AMBIANTA SI SCAZUTA
1.15. OTEL PENTRU AUTOTURISME DACIA
1.16. OTEL PENTRU TEVI UTILIZATE LA TEMPERATURI RIDICATE
1.17. OTEL CU GRANULATIE FINA PENTRU TABLE DESTINATE CONSTRUCTIILOR SUDATE
1.18. OTEL PENTRU TEVI UTILIZATE LA TEMPERATURI SCAZUTE
1.19. OTEL PENTRU TABLE SI BENZI DESTINATE AMBUTISARII
1.20. OTEL PENTRU TABLE SI BENZI LAMINATE LA RECE DESTINATE CAROSERIILOR AUTO
1.21. OTEL REZISTENT LA COROZIUNE
1.22. OTEL PENTRU AUTOMATE
1.23. OTEL PENTRU PINIOANE
1.24. OTEL PENTRU ORGANE DE ASAMBLARE
1.25. OTEL PENTRU TEVI FARA SUDURA, DE UZ GENERAL
1.26. OTEL PENTRU SUPAPELE MOTOARELOR CU ARDERE INTERNA
1.27. OTEL PENTRU SUPAPE EVACUARE
1.28. OTEL TERMOREZISTENT PENTRU ORGANE DE SAMBLARE
2. OTELURI TURNATE
2.1. OTEL SLAB ALIAT SI ALIAT TURNAT IN PIESE
2.2. OTEL AUSTENITIC MANGANOS TURNAT IN PIESE
2.3. OTEL TURNAT IN PIESE PENTRU ARMATURI
2.4. OTEL CARBON, SLAB ALIAT REZISTENT LA TEMPERATURI RIDICATE, TURNAT IN PIESE
3. FONTE
3.1. FONTE CU GRAFIT LAMELAR
3.2. FONTE CU GRAFIT NODULAR
3.3. FONTE MALEABILE
3.4. FONTE CU GRAFIT NODULAR CU STRUCTURA BAINITICA
1. oteluri
Recomandari de utilizare:
• Corespondenta marcilor de oteluri laminate sau trase este in conformitate cu STAS R 4400/1-80.
• Corespondenta indicata este aproximativa si data cu titlu informativ. Ea este stabilita pe baza : compozitiei chimice, caracteristicilor mecanice si a conditiilor de utilizare.
• Pentru marcile straine indicate intre paranteze corespondenta stabilita este foarte larga.
1.1. OTEL DE UZ GENERAL PENTRU CONSTRUCTII
STAS 500/2-80 NF
A 35-501-77
DIN 17100
Marca Numar
OL 34.1 A 34-1 USt 34-11.0055
OL 37.1
OL 37.2
OL 37.2k
OL 37.3
OL 37.4
E 24-1
E 24-2 (S235JR)
E 24-2NE
E 24-3
E 24-4
USt 37-1
USt 37-2
RSt 37-2
St 37-3
St 37-3
1.0065
1.0036
1.0038
1.0116
1.0116
OL 42.1
OL 42.1k
OL 42.2
OL 42.2k
OL 42.3
-
E 26-1
E 26-1NE
E 26-2
E 26-2NE
E 26-3
E 26-4
USt 42-1
RSt 42-1
USt 42-2
RSt 42-2
St 42-3
St 42-3
1.0075
1.0077
1.0040
1.0042
1.0136
1.0136
OL 44.2(k)
OL 44.3(k)
OL 44.4(k)
E 30-2
E 30-3
E 30-4
RSt 46-2
St 46-3
St 46-3
1.0477
1.0483
1.0483
OL 52.2(k)
OL 52.3(k)
OL 52.4(k)
E 36-2
E 36-3
E 36-4
-
St 52-3
St 52-3
-
1.0570
1.0570
OL 50(k) A 50-2 St 50-2 1.0050
OL 60(k) A 60-2 St 60-2 1.0060
OL 70(k) A 70-2 St 70-2 1.0070
OL 30 A 33-1
A 33-2
St 33-1
St 33-2
1.0033
1.0035
1.2. OTEL CARBON DE CALITATE PENTRU TRATAMENT TERMIC, DESTINAT CONSTRUCTIEI DE MASINI
STAS 880-80NF
A 35-551-72
A 35-552-72
DIN
17200-69
17210-69
Marca Numar
OLC 10
OLC 10 X
CC 10 , (AF 34 C 10)*
XC 10
C 10
Ck 10
1.0301
1.1121
OLC 15
OLC 15 X
AF 37 C 12)*
XC 18, (XC 15)
C 15
Ck 15
1.0401
1.1141
OLC 20 CC 20 - -
OLC 25
OLC 25 X
(AF 42 C 20)*
XC 25, (XC 18)
C22
Ck 22
1.0402
1.1151
OLC 35
OLC 35 X
CC 35, (AF 55 C 35)*
XC 38, (XC 35), (XC 32)
C 35
Ck 35
1.0501
1.1181
OLC 45
OLC 45 X
CC 45,(AF 65 C 45)*
XC 48, (XC 45), (XC 42)
C 45
Ck 45
1.0503
1.1191
OLC 55
OLC 55 X
XC 55, (XC 54) C 55
Ck 55
1.0535
1.1203
OLC 60
OLC 60X
(AF 70 C 55)*
XC 60, (XC 65)
C 60
Ck 60
1.0601
1.1221
*simbolizare veche
1.3. OTEL PENTRU ARCURI
STAS 795-80 NF
A 35-551-72
A 35-552-72
A 35-571-74
DIN
17221-72
17222-72
Marca Numar
OLC 55 A XC 55 Ck 551.1203
OLC 65 A
(OLC 66 S
STAS 8371-80)
XC 68 (XC 65) Ck 67 1.1231
OLC 75 A XC 75 Ck 75 1.1248
OLC 85 A - Ck 85 1.1269
51 Si 17 A 51 S 7 51 Si 7 1.0903
40 Si 17 A (45 S 7) - -
51 VCr 11 A 50 CV 4 50CrV 4 1.8159
56 Si 17 A 55 S 7 55 Si 7 1.0904
60 Si 15 A - 60SiCr7 1.7108
65 S 2 WA
(STAS 11514-80)
- - -
1.4. OTEL ALIAT PENTRU TRATAMENT TERMIC IN CONSTRUCTIA DE MASINI
STAS 791-80 NF
A 35-551-72
A 35-552-72
A 35-571-74
DIN
17210-69
17200-69
Marca Numar
15 Cr 08- (15 Cr 3) 1.7015
18 MnCr 1016 MC 5
16 MnCr 5 1.7131
21 MoMnCr 12 (18 CD 4) - -
18 MoCrNi 1318 NCD 6
18 CND 6
17 CrNiMo 6 1.6587
13 CrNi 30 (14 NC 11)
(16 NC 11)
(14 NiCr 10) 1.5732
20 MoNi 35 - - -
21 TiMnCr 12 - - -
28 TiMnCr 12 - - -
35 Mn 16 - - -
65 Mn 10 - 65 Mn 4 1.2817
35 MnSi 12 - 37 MnSi 5 1.5122
40 Cr 10 42 C 4 41 Cr 4 1.7035
40 BCr 10 - - -
33 MoCr 11 34 CD 4
(35 CD 4)
34 CrMo 4 1.7220
41 MoCr 11 (38 CD 4)
40 CD 4
42 CD 4
42 CrMo 4 1.7225
50 VCr 11 50 CV 4 50 CrV 4 1.8159
34 MoCrNi 15 (35 NCD 6) 34 CrNiMo 8 1.6582
30 MoCrNi 20 30 CND 8
30 NCD 8
30 CrNiMo 8 1.6580
38 MoCrAl 09 (40 CAD 6.12) (34 CrAlMo 5)
(41 CrAlMo 7)
1.8507
1.8509
41 CrNi 12 (30 NC 12) (31 NiCr 14) 1.5752
18 CrNi 20 20 NC 6 18 CrNi 8 1.5920
1.5. OTEL RAPID DE SCULE
STAS 7382-80 NF
A 35-590-78
SEW
320-69
Marca Numar
Rp 1- - -
Rp 2 Z 80 WKCV 18.05.04.01HS 18-1-2-5
1.3255
Rp 3 (Z80 WCV 18.04.01) HS 18-0-1 1.3355
Rp 5 Z 85 WDCV 06.05.04.02 HS 6-5-2C 1.3343
Rp 9 - HS 3-3-2 1.3333
Rp 10 Z 85 DCWV 08.04.02.02 HS 2-9-1 1.3346
- Z 110 WKDV 07.05.04.02 HS 7-4-2-5
- Z 120 WDV 06 HS 6-5-3
- Z 150 WKV 12 HS 12-4-5-5
- Z 110 DKWV 09.08.02.01 HS 2-9-1-8
- Z 160 WDV 06 HS 6-5-3
- Z 110 DK 09 (lame de forma, scule GLEASON)
1.6. OTEL PENTRU SCULE
STAS 1700-80 NF
A 35-590-78
SEW
150-71
Marca Numar
OSC 7 Y1 70(C 67 W3) 1.1744
OSC 8 Y1 80
Y1 90
C 80 W 1
C 80 W 2
1.1525
1.1625
OSC 10 Y1 105 (C 105 W 1)
(C 105 W 2)
1.1545
1.1645
OSC 11 - C 110 W 2 1.1654
OSC 13 -
-
-
(C 125 W 1)
(C 125 W 2)
(C 135 W 2)
1.1560
1.1663
1.1673
1.7. OTEL ALIAT PENTRU SCULE
STAS 3611-80NF
A 35-590-78
SEW 200-69
SEW 250-70
Marca Numar
MCV 14 105 WC 13 105 WCr 61.2419
VM 18 90 MV 8 90 MnCrV 8 1.2842
CW 20(105 WC 13) (105 WCr 6) 1.2419
C 120 Z 200 C 12 X 210 Cr 12 1.2080
VMoC 120 Z 160 CDV 12 X 153 CrMoV 12 1.2601
CV 06 - 115 CrV 3 1.2210
VCW 85 Z 30 WCV 9 X 30 WCrV9 3 1.2581
MoCN 15 - 55 NiCrMoV 6 1.2713
VMoCN 17 55 NCDV 7 56 NiCrMoV 7 1.2714
MoVC 30 32 DCV 5 X 32 CrMoV 3 3 1.2365
- 35 CDV 5 X 100 CrMoV 5
MoVC 50.10 Z 38 CDV 5 X 37 CrMoV 5 1 1.2343
MoVC 50.13 Z 40 CDV 5 X 40 Cr MoV 5 1 1.2344
MoWC 53 - X 37 CrMoW 5 1 1.2606
VSCW 20 - 45 WCrV 7 1.2542
1.8. OTEL REZISTENT LA COROZIUNE SI REFRACTAR, PRELUCRAT LA CALD
STAS 3583-80NF
A 35-572-75
A 35-578-70
DIN 17440-72
SEW 470-76
Marca Numar
12 Cr 130Z 12 C 13 X 10 Cr 13 1.4006
20 Cr 130 Z 20 C 13 X 20 Cr 13 1.4021
30 Cr 130 Z 30 C 13 X 30 Cr 13 1.4028
40 Cr 130 - X 40 Cr 13 1.4034
8 (Ti)Cr 170 Z 8 C 17 X 8 Cr 17
X 6 Cr Ti 17
1.4016
1.4510
12 NiCr 180 (Z 10 CN 18.09) X 12 CrNi 18 8 1.4300
10 TiNiCr 180
(STAS 10322-80)
Z 6 CNT 18.10 X 10 CrNiTi 18 9 1.4541
10 TiMoNiCr 175 Z 6 CNDT 17.12 X 10 CrNiMoTi 18 10 1.4571
15 SiNiCr 250
(Cr 25 Ni 20
STAS 11510-80)
Z 12 CNS 25.20 X 15 CrNiSi 25 20 1.4841
1.9. OTEL INOXIDABIL SI REFRACTAR
STAS 11523-80 NF
A 35-572-75
A 35-576-75
A 35-578-70
A 35-583-75
DIN 1770-72
SEW 400-73
SEW 470-76
SEW 670-69
Marca Numar
7 AlCr 130 Z 6 CA 13
X 7 CrAl 13 1.4002
22 NiCr 170 Z 15 CN 16.02 X 22 CrNi 17 1.4057
90 VmoCr 180 Z 100 CD 17 X 90 CrMoV 18 1.4112
35 MoCr 165 - X 35 CrMo 17 1.4122
2 NiCr 185 Z 2 CN 18.09
Z 2 CN 18.10
X 2 CrNi 18 9 1.4306
2 MoNiCr 175 Z 2 CND 17.12 X 2 CrNiMo 18 12 1.4435
2 CuMoCrNi 250 Z 1 NCDU 25.20 (X 2 NiCrMoCu 25 21) 1.4536
10 AlCr 240 Z 10 CAS 24 X 10 CrAl 24 1.4762
15 SiNiCr 200 Z 15 CNS 20.15 X 15 CrNiSi 20 12 1.4828
12 NiCr 250 Z 12 CN 25.20 X 12 CrNi 25 21 1.4845
2 NiCr 250 Z 2 CNNb 25.20 (X 5 CrNi 25 21) 1.4335
12 SiCrNi 360 Z 12 NCS 35.16 X 12 NiCrSi 36 16 1.4864
40 SiCrNi 380 - X 40 NiCrSi 36 16 1.4865
10 TiAlCrNi 320 - X 10 NiCrAlTi 32 20 1.4876
12 TiNiCr 180 Z 6 CNT 18.12 B X 12 CrNiTi 18 9 1.4878
19 MoCr 120 - X 19 CrNiTi 12 1 1.4921
20 VWMoCr 120 - X 20 CrMoWV 12 1 1.4935
(5 NiCr 180) Z 6 CN 18.09
Z 6 CN 18.10
X 5 CrNi 18 9
X 5 CrNi 18 10
1.4301
1.10. OTEL PENTRU RULMENTI
STAS 1456/1-80NF
A 35-565-70
SEW 350-53
Marca Numar
RUL 1100 C 6 100 Cr 6 1.3505
RUL 2 - 100 CrMn 6 1.3520
1.11. OTEL REZISTENT LA UZURA
STAS 11513-80 NF
A 35-551-72
A 35-552-72
DIN
17200-69
17115-72
Marca Numar
20 Mn 10(20 M 5) 28 Mn 6 1.1170
40 Mn 10 (35 M 5) 40 Mn 4 1.1157
1.12. OTEL PENTRU TABLE GROASE DESTINATE RECIPIENTILOR SUB PRESIUNE, CU CONDITII SPECIALE DE CALITATE
STAS 11502-80 NF
A 35-501-77
A 35-201-75
SEW 089-70
Marca Numar
RV 52E 355 TTStE 36 1.0566
R 55 E 420 TTStE 43 1.8912
R 58 E 460 TTStE 47 1.8915
09 Mn 16 E 30-3
E 30-4
- -
1.13. OTEL PENTRU TABLE DESTINATE CAZANELOR SI RECIPIENTELOR SUB PRESIUNE, PENTRU TEMPERATURA AMBIANTA RIDICATA
STAS 2883/3-80 NF
A 36-205-79
A 36-206-78
DIN 17155-59
Marca Numar
K 41A 42 CP H II 1.0425
K 47 A 48 CP 17 Mn 4 1.0481
K 52 A 52 CP 19 Mn 5 1.0482
16 Mo 3 15 D 3 15 Mo 3 1.5415
14 CrMo 4 15 CD 4.05 13 CrMo 4 4 1.7335
1.14. OTEL PENTRU TABLE DESTINATE CAZANELOR SI RECIPIENTELOR SUB
PRESIUNE, PENTRU TEMPERATURA AMBIANTA SCAZUTA
STAS 2883/2-80NF
A 36-205-79
A 36-208-79
DIN 17135-64
SEW 089-70; SEW 680-70
Marca Numar
R 37A 37 AP ASt 35
TTSt 35
1.0346
1.0356
R 44 A 48 AP
A 48 FP
(05 N 285)
ASt 45
TTSt 41
TTStE 29
1.0436
1.0437
1.0488
R 52 A 52 AP
A 52 FP
(05 N 355)
ASt 52
TTStE 36
1.0577
1.0566
1.15. OTELURI PENTRU AUTOTURISMELE DACIA 1300
STAS 11500/2-80NF
A 35-551-72
A 35-552-72
A 35-571-74
DIN
17200-69
17210-69
17221-72
Marca Numar
38 Cr 0538 C 2 38 Cr 2 1.7003
OLC 42 XC 42 - -
32 Cr 10 32 C 4 32 Cr 4 1.7033
37 Cr 10 38 C 4 37 Cr 4 1.7034
12 MoCr 10 - (13 CrMo 4) 1.7335
16 MoCr 10 16 CD 4
(18 CD 4)
- -
20 MoCr 10
20 CD 4 - -
30 MoCr 10 30 CD 4 - -
33 MoCr 10 34 CD 4
(35 CD 4)
34 MoCr 4 1.7220
20 NiCr 15 20 NC 6 (18 CrNi 8) 1.5920
35 MoCrNi 40 35 NCD 16 - -
16 CrMn 12 16 MC 5 16 MnCr 5 1.7131
X 61 SC 7 60 SiCr 7 1.0961
1.16. OTEL PENTU TEVI UTILIZATE LA TEMPERATURI RIDICATE
STAS 8184-80 NF
A 49-811-73
A 36-206-78
DIN
17115-59
Marca Numar
OLT 35 KTU 37- C St 35.8 1.0305
OLT 45 K TU 48-C St 45.8 1.0405
16 Mo 3 15 D 3 15 Mo 3 1.5415
14 CrMo 4 15 CD 4.05 13 CrMo 4 4 1.7335
10 CrMo 10 10 CD 9.10 10 CrMo 9 10 1.7380
16 MoCr 50 - 12 CrMo 19 5 1.7362
1.17. OTEL CU GRANULATIE FINA PENTRU TABLE DESTINATE CONSTRUCTIILOR SUDATE
STAS 9021-80NF
A 36-201-75
SEW 089-70
Marca Numar
OCS 44- TTStE 29 1.0488
OCS 52 E 355 TTStE 36 1.0566
OCS 55 E 420 TTStE 43
WstE 43
1.8932
1.8912
OCS 58 E 460 TTSt E 47
WstE 47
1.8915
1.8935
1.18. OTEL PENTRU TEVI UTILIZATE LA TEMPERATURI SCAZUTE
STAS 10382-80NF
A 36-208-79
SEW 680-70
Marca Numar
OLT 35 R- TTSt 35 1.0356
OLT 45 R - - -
10 Ni 35 (3,5 N 355) 10 Ni 14 1.5637
1.19. OTEL PENTRU TABLE SI BENZI DESTINATE AMBUTISARII
STAS 9485-80NF DIN 1623-72
A 36-401-69
A 35-301-71
Marca Numar
A 1 TC St 12 1.0330
A 2 E St 13 1.0333
A 3 (ES) St 14 1.0338
A 3 Ck
(STAS 11509-80)
3 C St W 24 1.0335
1.20. OTEL PENTRU TABLE SI BENZI LAMINATE LA RECE, DESTINATE CAROSERIILOR AUTO
STAS 10318-80NF
A 36-401-69
DIN 1623-72
Marca Numar
A 4E (St 13) 1.0333
A 5 ES (St 14) 1.0338
1.21. OTELURI REZISTENTE LA COROZIUNE
STAS 500/3-80NF
A 35-502-79
RCA 37 (E 24 W)
RCA 52 (E 36 WB)
1.22. OTEL PENTRU AUTOMATE
STAS 1350-80 NF
A 35-562-78
DIN 1651-70
Marca Numar
AUT 12(10 F 1) (10 S 2) 1.0721
AUT 20 - (22 S 20) 1.0724
AUT 30 - (35 S 20) 1.0726
AUT 40 M (45 MF 6) (45 S 20) 1.0727
1.23. OTEL PENTRU PINIOANE
STAS 11512-80 NF
A 35-551-72
A 35-552-72
DIN 17210-69
Marca Numar
17 CrNiMo 618 NCD 6 17 CrNiMo 6 1.6587
1.24. OTEL PENTRU ORGANE DE ASAMBLARE
STAS 11511-80NF
A 35-551-72
A 35-552-72
DIN (norma tehnica interna)
Marca Numar
20 MnB 520 MB 5 20 MnB 3 1.5507
1.25. OTEL PENTRU TEVI FARA SUDURA, DE UZ GENERAL
STAS 8183-80 NF DIN 1629-61
MarcaNumar
OLT 35 St 35 1.0308
OLT 45 St 45 1.0408
OLT 65 - -
1.26. OTEL PENTRU SUPAPELE MOTOARELOR CU ARDERE INTERNA
STAS 11311-80 NF
A 35-579-70
DIN (dupa norma interna)
Marca Numar
45 SiCr 85 Z 45 CS 9 (X 45 CrSi 9 3) 1.4718
1.27. OTEL PENTRU SUPAPE DE EVACUARE
STAS 11524-80 NF
A 35-579-70
DIN (dupa norma interna)
Marca Numar
45 SiCr 9545 CS 9 X 45 CrSi 9 3 1.4718
80 SiNiCr 200 Z 80 CSN 20.02 X 80 CrNiSi 20 1.4747
53 NNiMnCr 210 Z 52 CMN 21.09 X 53 CrMnNiN 21 9 1.4871
1.28. OTEL TERMOREZISTENT PENTRU ORGANE DE ASAMBLARE
STAS 11512-80 NF
A 35-558-69
DIN 17240-76
Marca Numar
24 VMoCr 1228 CDV 5.08 24 CrMoV 5 5 1.7733
12 MoCr 90 - X 12 CrMo 9 1 1.7386
2. OTELURI TURNATE
Recomandari de utilizare :
• Corespondenta marcilor de oteluri turnate este orientativa si in conformitate cu STAS R 4400/2-88,
• Corespondenta indicata este aproximativa si data cu titlu informativ. Ea este stabilita pe baza : compozitiei chimice, caracteristicilor mecanice si a conditiilor de utilizare.
2.1. OTEL SLAB ALIAT SI ALIAT TURNAT IN PIESE
STAS 1773-82 NF
A 32-054-78
A 32-055-76
TGL
14395-85
T 20 Mn 1420 M 6-M GS-20 Mn 6
T 35 Mn 14 30 M 6-M GS-35 Mn 6
T 40 Mn 11 - GS-45 Mn 4
T 30 SiMn 12 FC-M -
T 34 MoCr 09 25 CD 4-M GS-30 CrMo 4
T 35 MoCrNi 08 - -
T 26 VSiMn 14 30 MV6-M -
T 20 TiMn 12 - -
T 35 SiCrMn 11 - GS-40 MnCrSi 3
T 30 MoCrNi 14 30 NCD 8-M GS-30 CrNiMo 6
T 14 VMoCuNi 16 - -
T 40 VMn 17 - -
poansoane, lame ascutite : 50 CD 4-M
piese foarte solicitate la frecare :
32 NCD 14- M
matrite forja, scule de taiere si calibrare :
35 cdv 5-M
piese foarte solicitate cu duritate foarte ridicata :
Z160CDV 12- M
2.2. OTEL AUSTENITIC MANGANOS TURNAT IN PIESE
STAS 3718-87NF
A 32-058-84
DIN 17445-73
Marca Numar
T 105 Mn 120-
T 130 Mn 135 Z 120 M 12-M G-X 120 Mn 12
T 120 CrMn 130 Z 120 MC 12-M
T 100 NiMn 130Z 100 MN 13.4-M
T 100 MoMn 130 Z 110 MD 12.1-M
T 35 NiCr 260 (Z 40 CN 25.20-M) G-X 40 CrNiSi 25 12 1.4837
T 25 NiCr 250 G-X 15 CrNi 25 20 1.4840
T 35 CrNi 370 G-X 40 CrNiSi 36 18 1.4865
T 12 MoNiCr 210 - -
2.3. OTELURI TURNATE IN PIESE PENTRU ARMATURI
STAS 9277-84NF
A 32-055-76
A 32-056-84
DIN 17245-77
Marca Numar
OTA 20 A 42 C-M GS-C 25 1.0619
OTA 40Mn13 - - -
OTA 30VMn13 - - -
OTA 17MoCr13 15 CD 5.05-M GS-18CrMo9 10 1.7379
OTA 23VWMoCr120 - G-X22CrMoV12 1 1.4931
OTA 10NbMoNiCr170 Z 4 CNDNb 18.12-M G-X5CrNiMoNb18.10 1.4581
OTA 10TiMoNiCr170 - - -
2.4. OTEL CARBON, SLAB ALIAT SI MEDIU ALIAT REZISTENT LA TEMPERATURI RIDICATE, TURNAT IN PIESE
STAS 12404-85 NF
A 32-055-85
DIN 17245-75
Marca Numar
T 21 A 42 C-M GS-C 25 1.0619
T 16 Mo 5 - GS-22 Mo 4 1.5419
T 16 MoCr 11 15 CD 4.05-M GS-17 CrMo 5 5 1.7357
T 14 MoVCr 6 - - -
T 21 VMoCr 10 NCDV 4.10-M - -
T 17 VMoCr 14 15 CDV 9.10-M GS-17 CrMoV 5 11 1.7706
T 15 MoWVCr 12 - - -
Notatii utilizate:
• STAS –standard de stat Romania
• NF –norma Franta
• DIN, SEW – norme Germania
Simbolizarea elementelor chimice utilizate :
Denumirea in
l. romana
Simbolul dupa STAS
Simbol dupa NF
Simbol dupa
DIN, SEW
Aluminiu Al A Al
Nichel Ni N Ni
Molibden Mo D Mo
Crom Cr C Cr
Cupru Cu U Cu
Staniu Sn E Sn
Sulf (fosfor) S F S
Mangan Mn M Mn
Plumb Pb Pb Pb
Azot (nitrogen) N Az N
Siliciu Si S Si
Titan Ti T Ti
Tugsten W W W
Vanadiu V V V
Zinc Zn Z Zn
Zirconiu Zr ZR Zr
Bor B B B
Niobiu Nb Nb Nb
Cobalt Co K
3. FONTE
3.1. FONTE CU GRAFIT LAMELAR
SR ISO 185-94Simbol vechi
STAS 568-82
NF DIN
Marca Rm
N/mm2
Marca Numar
100 100 Fc 100 Ft 10 D GG-10 0.6010
150 150 Fc 150 Ft 15 D GG-15 0.6015
200 200 Fc 200 Ft 20 D GG-20 0.6020
250 250 Fc 250 Ft 25 D GG-25 0.6025
300 300 Fc 300 Ft 30 D GG-30 0.6030
350 350 Fc 350 Ft 35 D GG-35 0.6035
- 400 Fc 400 Ft 40 D GG-40 0.6040
FGL 175HB*
FGL 215HB*
FGL 240HB*
*Fonte prevazute pe echipamente RENAULT (E01.41.050.N):
3.2. FONTE CU GRAFIT NODULAR (SFEROIDAL)
SR ISO 5922-95 Simbol vechi
NF DIN
STAS 6071-82
Marca Rm
N/mm2
A
%
Marca Numar
Ft GjS 900-2 900 2 - - - -
800-2 800 2 Fgn 800-3 FGS 800.2 GGG-80 0.7080
700-2 700 2 Fgn 700-2 FGS 700.2 GGG-70 0.7070
600-3 600 3 Fgn 600-2 FGS 600.3 GGG-60 0.7060
- - FGS 600-3A*
500-7 500 7 Fgn 500-7 FGS 500.7 GGG-50 0.7050
450-10 450 10 Fgn 450-5 - (GGG-40.3) 0.7043
400-15 400 15 - (FGS 400.12) GGG-40 0.7040
400-18 350 18 - - - -
- - FGS 400-18A*
350-22 350 22 - (FGS 370.17) GGG-35.3 0.7033
*Fonte prevazute pe echipamente RENAULT (E01.45.030.N) :
3.3. FONTE MALEABILE
SR ISO 5922-95 Simbol
vechi
569-79
NF DIN
Marca Rm
N/mm2
A
%
Tip Marca Numar
W 35-04 350 4 cu Fma 350 (MB 35.7) GTW-35 0.8035
inima
alba
W 38-12 380 12 - - GTW-S38 0.8038
W 40-05 400 5 Fma 400 (MB 40.10) GTW-40 0.8040
W 45-07 450 7 - - GTW-45 0.8045
B 30-06 300 6 cu
inima
neagra
Fmn 300 - - -
B 32-12 320 12 Fmn 320 - - -
B 35-10 350 10 Fmn 350 MN 35.10 GTS-35 0.8135
P 45-06 450 6 perlitica
Fmp 450 GTS-45 0.8145
P 50-05 500 5 Fmp 500 - - -
P 55-04 550 4 Fmp 550 GTS-55 0.8155
P 60-03 600 3 Fmp 600 - - -
P 65-02 650 2 Fmp 650 GTS-65 0.8165
P 70-02 700 2 Fmp 700 MP 70.2 GTS-70 0.8170
P 80-01 800 1 -
3.4. FONTE CU GRAFIT NODULAR CU STRUCTURA BAINITICA
SR ISO 13169-94 Simbol
STAS
vechi
Marca Rm
N/mm2
A
%
HB
FgnB 800 800 10 260-320 nu exista
FgnB 900 900 8 280-340
FgnB 1000 1000 5 300-380
FgnB 1100 1100 3 360-420
FgnB 1200 1200 2 380-450
FgnB 1400 1400 - 450-550
Document Info
Accesari: 813 Apreciat:
Comenteaza documentul:
Nu esti inregistrat Trebuie sa fii utilizator inregistrat pentru a putea comenta
Creaza cont nou